Excellent quality Competitive Calcined Alumina Al2o3 - Low Sodium Calcined Alumina (CA) Series for Ceramics – Yufa
Excellent quality Competitive Calcined Alumina Al2o3 - Low Sodium Calcined Alumina (CA) Series for Ceramics – Yufa Detail:
Applications
| Model No. | Chemical Composition(%) | True Density | Apparent Density | Grain Size D50 | +325 Mesh | Original Crystal D50 | Features | Recommended Applications | ||||
| Al2O3 ≥% |
SiO2 ≤% |
Fe2O3 ≤% |
Na2O ≤% |
LOI ≤% |
g/cm3 ≥ |
g/cm3 ＞ |
D50 (μm) |
＜% | D50(μm) | |||
| CA1A | 99.5 | 0.05 | 0.03 | 0.10 | 0.1 | 3.97 | >0.95 | ~70 | 5.0-6.0 | 1. High temperature calcination 2. Low sodium 3. Large crystal 4. High conversion rate 5. Stable shrinkage. Good fluidity 6. High insulation performance 7. High mechanical strength |
1. High-performance ceramics, such as vacuum tubes 2. Especially suitable for hot -pressing casting process |
|
| CA1D | 99.5 | 0.05 | 0.03 | 0.08 | 0.1 | 3.95 | >0.90 | 3.0-4.0 | 1. Low sodium 2. Moderate crystal size 3. Good particle size distribution 4. Small shrinkage and stability |
1. Spark plugs 2. Vacuum tubes 3. Wear-resistant ceramics, etc. 4. More suitable for static pressure, dry-pressing and other forming processes |
||
| CA1 | 99.5 | 0.05 | 0.03 | 0.10 | 0.1 | 3.95 | >0.90 | 3.0-3.8 | 1. Static kiln calcination 2. Low sodium 3. Moderate crystal size 4. Good particle size distribution 5. High porcelain density |
1. Mainly used in electronic ceramics 2. Especially suitable for Hot die casting process |
||
| CA2 | 99.5 | 0.08 | 0.03 | 0.08 | 0.1 | 3.96 | >0.90 | 2.8-3.8 | 1. Low sodium 2. Strict crystal size control 3. Good fluidity 4. Stable shrinkage |
1. Electronic ceramics, structural ceramics 2. Especially suitable for Hot die casting process |
||
| CA2G | 0.15 | >0.90 | 3.0-3.5 | < 3.0 | 1. CA2 full grinding 2. Particle size control stability 3. Low sodium 4. Shrinkage stability |
1. Electronic ceramics 2. Structural ceramics, more suitable for making ceramic rollers |
||||||
| CA3 | 99.5 | 0.05 | 0.03 | 0.04 | 0.1 | 3.96 | >0.85 | ~70 | 2.0-2.6 | 1. Strict control of firing temperature 2. Small crystal size 3. Good particle distribution 4. Pretty-low sodium |
Suitable for electronic ceramics, such as IC substrates | |
| CA3G | 0.1 | 2.4-2.9 | <1.0 | Fully grinding of CA3 | ||||||||
| CA4 | 99.5 | 0.05 | 0.03 | 0.10 | 0.1 | 3.93 | >0.90 | ~70 | 1.0-1.8 | 1. Good activity 2. Low sodium 3. High density after firing 4. Stable shrinkage 5. High mechanical strength |
1. Structural ceramics 2. Electronic ceramics 3. 99 alumina ceramic granulation powder material 4. Suitable for extrusion molding process as well |
|
| CA4G | 0.1 | >0.60 | 1.5-2.2 | <1.0 | Fully grinding of CA4 | |||||||
| CA5 | 99.5 | 0.05 | 0.02 | 0.05 | 0.1 | 3.92 | ~70 | ＜1.0 | 1. Small & unifrom crystal size 2. Good activity |
99 alumina ceramic hot die casting process, etc | ||
| CA5G | 1-1.3 | <1.0 | 1. Small & unifrom crystal size 2. Good activity 3. Fully grinding 4. Narrow particle size distribution |
Ceramic filter,etc | ||||||||
Product detail pictures:
Related Product Guide:
We believe that prolonged expression partnership is really a result of top of the range, value added support, rich encounter and personal contact for Excellent quality Competitive Calcined Alumina Al2o3 - Low Sodium Calcined Alumina (CA) Series for Ceramics – Yufa , The product will supply to all over the world, such as: Ottawa, Italy, India, Since our establishment, we keep on improving our products and customer service. We are able to provide you with a wide range of high quality hair products at competitive prices. Also we can produce different hair products according to your samples. We insist on high quality and reasonable price. Except this, we provide best OEM service. We warmly welcome OEM orders and customers all over the world to cooperate with us for mutual development in the future.
By David from Iraq - 2017.11.20 15:58
A good manufacturers, we have cooperated twice, good quality and good service attitude.
By Gail from Luxembourg - 2017.11.11 11:41
Write your message here and send it to us